Cyfansoddiad 1.Cemegol
Math | C (mwyafswm) | Mn (mwyafswm) | P (mwyafswm) | C (mwyafswm) | Si (mwyafswm) | Cr (mwyafswm) | Ni (mwyafswm) | Mo. | Arall |
304 | 0.08 | 2.0 | 0.045 | 0.03 | 1.0 | 18-20 | 8-12 | - | |
304L | 0.03 | 2.0 | 0.045 | 0.03 | 1.0 | 18-20 | 8-12 | - | |
316 | 0.08 | 2.0 | 0.045 | 0.03 | 1.0 | 16-18 | 10-14 | 2-3 | - |
316L | 0.08 | 2.0 | 0.045 | 0.03 | 1.0 | 16-18 | 10-14 | 2-3 | - |
Priodweddau 2.Mecanyddol
Math | Uts | Cynnyrch | Elongation | Caledwch | Rhif DIN comprable | |
N / mm2 | N / mm2 | % | HRB | Wroyght | Cast | |
304 | 600 | 210 | 60 | 80 | 1.4301 | 1.4308 |
304L | 530 | 200 | 50 | 70 | 1.4306 | 1.4552 |
316 | 560 | 210 | 60 | 78 | 1.4401 | 1.4408 |
316L | 530 | 200 | 50 | 75 | 1.4406 | 1.4581 |
3. Ymwrthedd Cyrydiad Cemegol
A siarad yn gyffredinol, nid oes gan 304 o ddur gwrthstaen a 316 o ddur gwrthstaen fawr o wahaniaeth o ran ymwrthedd cyrydiad cemegol, ond maent yn wahanol mewn rhai cyfryngau penodol.
Mae dur gwrthstaen 304 a ddatblygwyd i ddechrau yn fwy sensitif i bwyntiau cyrydiad o dan amodau penodol. Gall ychwanegu molybdenwm 2-3% leihau'r sensitifrwydd hwn, sy'n arwain at 316. Yn ogystal, gall y molybdenwm hwn hefyd leihau cyrydiad rhai asidau thermoorganig.
Dur Di-staen Carbon 4.Low
Mae gwrthiant cyrydiad dur gwrthstaen austenitig yn gysylltiedig â'r haen amddiffynnol cromiwm ocsid a ffurfiwyd ar yr wyneb metel. Os caiff y deunydd ei gynhesu i 450 ℃ -900 ℃, bydd strwythur y deunydd yn newid a bydd carbid cromiwm yn ffurfio ar hyd ymyl y grisial. Felly, ni ellir ffurfio'r haen amddiffynnol o gromiwm ocsid ar ymyl y grisial, sy'n arwain at ostyngiad mewn ymwrthedd cyrydiad.
Felly datblygwyd dur gwrthstaen 304L a dur gwrthstaen 316L i wrthsefyll y cyrydiad hwn. Mae cynnwys carbon dur gwrthstaen 304L a dur gwrthstaen 316L yn is, oherwydd bod y cynnwys carbon yn cael ei leihau, felly ni fydd carbid cromiwm.